Efeito do acabamento e polimento sobre a topografia superficial de uma resina composta convencional e uma bulk fill / Effect of finishing and polishing on the surface topography of a conventional compound resin and a bulk fill / Efecto de acabado y pulido en la topografía superficial de una resina compuesta convencional y un llenado a granel

Introdução:As atuaisresinas Bulk-Fill apresentamcomovantagens e propriedades: menor tempo clínico, baixa contração de polimerização, maior translucidez, entre outros. Objetivo:Avaliar a topografia superficial de restaurações com diferentes tipos de resina composta antes e após submetê-las a diferentes sistemas de acabamento e polimento. Metodologia:Confecção de100 corpos de prova, sendo 50 de cada composto resinoso, apresentando cinco grupos (n=10) sorteados de forma aleatória, de acordo com o sistema de acabamento e polimento empregado. Foram utilizadas as resinas Filtek Z350 XT e a Bulk Fill Filtek One Bulk Fill e os sistemas de acabamento e polimento: Discos de Lixa Sof-Lex Pop On Kit;Discos Diamantado Espiral Sof-Lex; Ponta Enhance e Broca Carbide Multilaminada nº 0283F, que foram comparados com superfície deixada pela Tira de Poliester (Controle Negativo). Após 7 dias de armazenamento em água destilada, os corpos de provaforam submetidos aoMicroscópio Eletrônico de Varredura.Resultados:Os corpos de provada resina Bulk Fill tiveram como melhor resultado o sistema de acabamento e polimentocom broca carbidee resultado não satisfatório com discodiamantado espiral Sof-lex, enquanto a ponta Enhance e lixa Sof-lex Pop Ontiveram resultados semelhantes. Os corpos de prova da resina Filtek Z350 XT tiveram melhor aspecto visual de lisura no grupo controle negativoe pior resultado no grupo com disco diamantado espiral Sof-lex. Conclusões:Dessa forma, o sistema que apresentou melhor resultado foi a broca Carbidena resina Bulk Fill, enquanto a Filtek Z350 XT apresentou-se melhor no grupo controle. Porém, ainda são necessáriosestudos para se chegar em um protocolo de acabamento e polimento mais eficiente (AU).

Introduction:The current Bulk-Fill resins have the following advantages and properties: less clinical time, low polymerization shrinkage, greater translucency, among others.Objective:Toevaluate the topography of restorations with different types of composite resin before and after submitting them to different finishing and polishing systems.Methodology:Manufacture of 100 specimens, 50 of each resin compound, presenting five groups (n = 10) drawn at random, according to the finishing and polishing system employed. Filtek Z350 XT resins and Bulk Fill Filtek One Bulk Fill andfinishing and polishing systems were used: Sof-Lex Pop On Kit Sanding Discs; Diamond Spiral Sof-Lex Discs; Tip Enhance and Multilaminated Carbide Drill nº 0283F, which were compared with the surface left by the Polyester Strip (Negative Control). After 7 days of storage in distilled water, the specimens were submitted to a Scanning Electron Microscope.Results:The Bulk Fill resin specimens had the best result of the finishing and polishing system with carbide drill and unsatisfactory result with Sof-lex spiral diamond disc, while the Enhance tip and Sof-lex Pop On sandpaper had similar results. The Filtek Z350 XT resin specimens had a better visual aspect of smoothness in the negative control group and a worse result in the group with Sof-lex spiral diamond wheel.Conclusions:Thus, the system that showed the best result was the Carbide drill in Bulk Fill resin, while Filtek Z350 XT was better in the control group. However, studies are still needed to arrive at a more efficient finishing and polishing protocol (AU).

Introducción:Las actuales resinas Bulk-Fill tienen las siguientes ventajas y propiedades: menor tiempo clínico, baja contracción de polimerización, mayor translucidez, entre otras.Objetivo: Evaluar la topografía de restauraciones con diferentes tipos de resina compuesta antes y después de someterlas a diferentes sistemas de acabado y pulido.Metodología: Fabricación de 100 probetas, 50 de cada resina compuesta, presentando cinco grupos (n = 10) extraídos al azar, según el sistema de acabado y pulido empleado. Se utilizaron resinas Filtek Z350 XT y Bulk Fill Filtek One Bulk Fill y sistemas de acabado y pulido: Discos de lijado Sof-Lex Pop On Kit; Discos Sof-Lex en espiral de diamante; Broca Realce de Punta y Carburo Multilaminado nº 0283F, que fueron comparadas con la superficie dejada por la Tira de Poliéster (Control Negativo). Después de 7 días de almacenamiento en agua destilada, lasmuestras se sometieron a un Las muestras de resina Bulk Fill tuvieron el mejor resultado del sistema de acabado y pulido con broca de carburo y un resultado insatisfactorio con el disco de diamante en espiral Sof-lex, mientras que la punta Enhance y el papel de lija Sof-lex Pop On tuvieron resultados similares. Las muestras de resina Filtek Z350 XT tuvieron un mejor aspecto visual de suavidad en el grupo de control negativo y un peor resultado en el grupo con disco de diamante en espiral Sof-lex.Conclusiones: Así, el sistema que mejor resultado mostró fue la broca Carbide en resina Bulk Fill, mientras que Filtek Z350 XT fue mejor en el grupo control. Sin embargo, aún se necesitan estudios para llegar a un protocolo de acabado y pulido más eficiente (AU).

Influência do uso da proantocianidina em um adesivo autocondicionante: avaliação da resistência de união / Influence of the use of proanthocyanidinin a self-etching adhesive: evaluation of bond strength / Influenciadel uso de proantocianidinaem um adesivo autograbante: evaluación de la fuerza de unión

Introdução:Os sistemas adesivos possibilitama execução de restaurações estéticas e minimamente invasivas, sendo, portanto,objeto de pesquisas para contornar os problemas que se apresentam no procedimento restaurador.Objetivo:Avaliar in vitroa resistência de união de um sistema adesivo autocondicionante, e deste modificado com soluções extrativas de semente de uva.Metodologia:Duas soluções extrativas foram preparadas comextrato de semente de uva em pó dissolvido em acetona e etanol. A partir delas e de umadesivo,seis sistemas adesivos autocondicionantes experimentais foram preparados, diferindo quanto aosolvente utilizado eàsproporções entre adesivo puro e solução extrativa(7,5%, 15% e 30%). Setenta incisivos bovinos hígidos tiveram as raízes removidas com disco de carborundum e as faces vestibulares desgastadas comlixas d'água de granulação 120, 240, 600 e 1200 sob refrigeração até expor a dentina superficial. Os dentes foram distribuídos aleatoriamenteem sete grupos distintos: Controle; A7,5; A15; A30; E7,5; E15; e E30, contendo 10 elementos cada. A aplicação dos adesivos foi executada de acordo com as recomendações do fabricante do adesivo controle. A restauração foi realizada com uma matriz de silicone com dimensões 2mm de altura e 4mm de diâmetro e inserido o material restaurador em incremento único e fotopolimerizado por 40s. Após três meses armazenados em água destilada, os espécimes foram submetidos ao teste de resistência de união. Foi empregado ométodo estatísticoTeste Paramétrico Anova 1 Fator e pós-teste de Tamhane (p<0,05). Resultados:Os grupos A7,5, E7,5 e E30 não apresentaram diferença em relação ao grupo Controle; A15 e A30 mostraram desempenho estatisticamente semelhante entre si; e E15 não apresentou diferença estatística em relação aos outros adesivos.Conclusões:A adição de proantocianidina teve efeitos diferentes,dependendodos solventes e das concentrações utilizadas, mas sem alterar significativamente o desempenho do adesivo (AU).

Introduction:Adhesive systems make it possible to perform aestheticand minimally invasive restorations, being the subject of research to circumvent the problems that arise in the restorative procedure.Objective:Evaluate in vitrothe bond strength of a self-etching adhesive system,and modified with extractive grape seed solutions. Methodology:Two extractive solutions were prepared with powdered grape seed extract dissolved in acetone and ethanol. From them and an adhesive, six experimental self-etching adhesive systems were prepared, differing in terms of the solvent used and the proportions between pure adhesive and extractive solution(7.5%, 15% and 30%). Seventy healthy bovine incisors had their roots removed with carborundum disc and the vestibular faces were worn with sandpaper with granulation water 120, 240, 600 and 1200 under refrigeration until the superficial dentin was exposed. The teeth were randomly assigned to seven different groups: Control; A7.5; A15; A30; E7.5; E15; and E30, containing 10 elements each. The application of the adhesives was carried out according to the recommendations of the manufacturer of the control adhesive. The restoration was performed with a silicone matrix with dimensions 2mm high and 4mm indiameter and the restorative material was inserted in a single increment and light cured for 40s. After three months stored in distilled water, the specimens were submitted to the bond strength test. The statistical method Parametric Test Anova 1 Factor and Tamhane post-test (p<0.05) were used. Results:Groups A7.5, E7.5 and E30 showed no difference in relation to the Control group; A15 and A30 showed a statistically similar performance; and E15 showed no statistical difference in relation to the other adhesives. Conclusions:The addition of proanthocyanidin had different effects, depending on the solvents and concentrations used, but without significantly altering the performance ofthe adhesive (AU).

Introducción: Sistemas adhesivos permiten realizar restauraciones estéticas y mínimamente invasivas, siendo objeto de investigación para sortear problemas que surgen en elprocedimiento restaurador. Objetivo: Evaluar in vitrola fuerza de unión de un sistema adhesivoautograbante y modificado con soluciones extractivas de semilla de uva. Metodología: Se prepararon dos soluciones extractivas con extracto de semilla de uva en polvo disuelto en acetona y etanol. A partir de ellos y de un adhesivo, se prepararon seis sistemas experimentales de adhesivos autograbantes, que se diferencian en cuanto al solvente utilizado y las proporciones entre adhesivo puro y solución extractiva (7,5%, 15% y 30%). Setenta incisivos bovinos sanos fueron removidos con un disco de carborundo y las caras vestibulares fueron usadas com lija de agua de granulación 120, 240, 600 y 1200 bajo refrigeración hasta que la dentina superficial quedo expuesta. Los dientes se asignaron aleatoriamente a siete grupos diferentes: Control; A7,5; A15; A30; E7,5; E15; y E30, que contiene 10 elementos cada uno. La aplicación de los adhesivos se realizó siguiendo las recomendaciones del fabricante del adhesivo de control. La restauración se realizó con matriz de silicona con 2mm de altura y 4mm de diámetro y el material restaurador se insertó en un solo incremento y se fotopolimerizó durante 40s. Tres meses después, almacenados em agua destilada, las muestras se sometieron a la prueba de resistencia de la unión. Se utilizó el método estadístico Prueba Paramétrica Factor Anova 1 y post-prueba de Tamhane (p<0,05). Resultados: Los grupos A7,5, E7,5 y E30 no mostraron diferencias em relación con el grupo Control; A15 y A30 mostraron un desempeño estadísticamente similar; y E15 no mostró diferencia estadística en relación con los otros adhesivos. Conclusiones: La adición de proantocianidina tuvo diferentes efectos, dependiendo de los disolventes y concentraciones utilizadas, pero sin alterar significativamente el rendimiento del adhesivo (AU).

Surface morphology changes of acrylic resins during finishing and polishing phases

INTRODUCTION: The finishing and polishing phases are essential to improve smoothness and shining on the surface of acrylic resins used to make removable orthodontic appliances. A good surface finishing reduces roughness, which facilitates hygiene, prevents staining and provides greater comfort to the patients. OBJECTIVE: The aim of this paper was to analyze the changes on surface morphology of acrylic resins during finishing and polishing phases. METHODS: Thirty discs (10 mm in diameter and 5 mm in length) were made with acrylic resin and randomly divided into ten groups. The control group did not receive any treatment while the other groups received gradual finishing and polishing. The last group received the entire finishing and polishing procedures. Surface morphology was qualitatively analyzed through scanning electron microscopy and quantitatively analyzed through a laser profilometer test. RESULTS: The acrylic resin surfaces without treatment showed bubbles which were not observed in the subsequent phases. Wearing out with multilaminated burs, finishing with wood sandpaper and finishing with water sandpaper resulted in surfaces with decreasing irregularities. The surfaces that were polished with pumice and with low abrasive liquids showed high superficial smoothness. CONCLUSION: Highly smooth acrylic resin surfaces can be obtained after mechanical finishing and polishing performed with multilaminated burs, wood sandpaper, water sandpaper, pumice and low abrasive liquids.

INTRODUÇÃO: as etapas de acabamento e polimento são essenciais para a obtenção de lisura e brilho da superfície de resinas acrílicas utilizadas na confecção de aparelhos ortodônticos. O bom acabamento da resina facilita a higiene, previne o manchamento e propicia maior conforto ao paciente. OBJETIVO: o objetivo desse trabalho foi analisar as alterações na morfologia superficial de resinas acrílicas (Clássico, São Paulo) durante as etapas do acabamento e polimento mecânico. MÉTODOS: foram confeccionados 30 discos (10mm de diâmetro e 5mm de altura) de resina acrílica autopolimerizável, que foram divididos aleatoriamente em dez grupos. O grupo controle não recebeu nenhum tratamento. Os demais grupos receberam acabamento e polimento graduais. O último grupo recebeu todo o tratamento de acabamento e polimento. A morfologia superficial foi avaliada qualitativamente por microscopia eletrônica de varredura e quantitativamente pela análise da rugosidade superficial. RESULTADOS: as superfícies de resina acrílica sem tratamento apresentaram bolhas, as quais não foram observadas nas fases subsequentes. O desgaste com fresa multilaminada seguido de acabamento com lixa de madeira e lixa d'água produziram superfícies com irregularidades decrescentes. As superfícies polidas com branco de Espanha e líquido de baixa abrasividade (Kaol) apresentaram bom acabamento superficial. CONCLUSÃO: é possível obter resina acrílica com alta lisura superficial após acabamento e polimento mecânico com fresas, lixas de madeira, lixas d'água, branco de Espanha e líquidos de baixa abrasividade (Kaol).

One-Year Evaluation of a Simplified Ethanol-Wet Bonding Technique: A Randomized Clinical Trial

The objective of this randomized clinical trial was to evaluate the clinical performance of adhesive restorations using a three-step etch-and-rinse adhesive (TSER), a one-step self-etching adhesive (OSSE), and a simplified ethanol-wet bonding technique (EWBT) prior to the application of a composite resin in non-carious cervical lesions. Ninety-three restorations (31 for each group) were placed in 17 patients by a single operator. No cavity preparation was performed. After 6 and 12 months, the restorations were assessed by two previously trained examiners using modified Ryge criteria for retention (kappa=1.00) and marginal adaptation/staining (kappa=0.81), and the results were analyzed by Fisher's exact and Kruskal-Wallis tests, respectively. No significant differences were observed among groups at the 6- and 12-month time points for any of the assessed criteria (p≥0.05). The intra-group analysis performed by Cochran's test (for retention) and Wilcoxon test (for marginal adaptation/staining) revealed significant differences between the baseline/12-month time intervals in marginal adaptation in OSSE (p=0.0180) and in marginal staining in TSER (p=0.0117). The survival analysis for retention criteria performed using a log-rank test did not show significant differences (p>0.05). The restorations placed using the simplified EWBT performed equally well as the other adhesive strategies employed.

O objetivo deste ensaio clínico randomizado foi avaliar o comportamento clínico das restaurações adesivas, usando um adesivo convencional de três passos (CTP), um adesivo autocondicionante de um passo (AUP) e uma técnica simplificada da adesão úmida por etanol (AUET) antes da aplicação de uma resina composta em lesões cervicais não-cariosas. Noventa e três restaurações (31 para cada grupo) foram realizadas em 17 pacientes por um único operador. Nenhum preparo cavitário foi realizado. Depois de 6 e 12 meses, as restaurações foram avaliadas por 2 examinadores previamente treinados, utilizando critérios de Ryge modificados para retenção (kappa=1,00) e adaptação/manchamento marginal (kappa=0,81), e os resultados foram analisados pelos testes Exato de Fisher e Kruskal-Wallis, respectivamente. Não foram observadas diferenças significativas entre os grupos aos 6 e 12 meses para qualquer um dos critérios avaliados (p≥0,05). A análise intra-grupo feita pelos testes Q de Cochran (para retenção) e Wilcoxon (para adaptação/manchamento marginal) revelou diferenças significativas entre os intervalos de tempo baseline/12 meses para a adaptação marginal no AUP (p=0,0180) e manchamento marginal no CTP (p=0,0117). A análise de sobrevivência para o critério retenção realizada utilizando o teste de log-rank não apresentou diferenças significantes (p≥0,05). As restaurações feitas utilizando a técnica simplificada da adesão úmida por etanol comportaram-se igualmente às outras estratégias adesivas empregadas.

Influence of core-finishing intervals on tensile strength of cast posts-and-cores luted with zinc phosphate cement

The core finishing of cast posts-and-cores after luting is routine in dental practice. However, the effects of the vibrations produced by the rotary cutting instruments over the luting cements are not well-documented. This study evaluated the influence of the time intervals that elapsed between the cementation and the core-finishing procedures on the tensile strength of cast posts-and-cores luted with zinc phosphate cement. Forty-eight bovine incisor roots were selected, endodontically treated, and divided into four groups (n = 12): GA, control (without finishing); GB, GC, and GD, subjected to finishing at 20 minutes, 60 minutes, and 24 hours after cementation, respectively. Root canals were molded, and the resin patterns were cast in copper-aluminum alloy. Cast posts-and-cores were luted with zinc phosphate cement, and the core-finishing procedures were applied according to the groups. The tensile tests were performed at a crosshead speed of 0.5 mm/min for all groups, 24 hours after the core-finishing procedures. The data were subjected to one-way analysis of variance (ANOVA) and Tukey's test (α = 0.05). No significant differences were observed in the tensile strengths between the control and experimental groups, regardless of the time interval that elapsed between the luting and finishing steps. Within the limitations of the present study, it was demonstrated that the core-finishing procedures and time intervals that elapsed after luting did not appear to affect the retention of cast posts-and-cores when zinc phosphate cement was used.

Changes in surface roughness and color stability of two composites caused by different bleaching agents

The objective of this study was to evaluate the effect of two bleaching agents (10% and 35% hydrogen peroxide) on the color stability and surface roughness of two composites, one nanohybrid and one nanoparticle. Specimens were polished, aged, stained, bleached and polished again. The action of the bleaching agents on the composites was analyzed using a profilometer (surface roughness) and a spectrophotometer (color stability). The effect of polishing the composites on the surface roughness and the resumption of the composite color was also evaluated. The results were analyzed statistically by ANOVA and Tukey's test at 5% significance level. The analysis indicated that the nanohybrid composite was more affected by staining. The bleaching agents were not able to promote bleaching of either composite over the evaluation period. Surface polishing returned nanohybrid composite to its original color condition, which did not occur for the nanoparticle composite. Additionally, polishing did not return the surface roughness of either composite to its original value. It may be concluded that polishing surface after bleaching should not be the treatment of choice, as it was not possible to reverse the roughness of the composites to their original values, suggesting that a more extensive and irreversible degradation might have occurred.

O objetivo deste estudo foi avaliar o efeito de dois agentes clareadores (peróxido de hidrogênio a 10% e 35%) sobre a estabilidade de cor e rugosidade superficial de dois compósitos, um nanohíbrido e um nanoparticulado. Os espécimes foram polidos, envelhecidos, manchados, clareados e polidos novamente. A ação dos agentes clareadores sobre os compósitos foi analisada em perfilômetro (rugosidade) e um espectrofotômetro (estabilidade de cor). A ação de polimento dos compósitos sobre a rugosidade superficial e a retomada da cor dos compósitos também foi avaliada. Os resultados foram analisados estatisticamente por ANOVA e teste de Tukey (5% de significância). A análise indicou que o compósito nanohíbrido foi mais afetado pelo manchamento. Os agentes clareadores não foram capazes de promover o clareamento dos compósitos ao longo do período de avaliação. O polimento da superfície retornou o compósito nanohíbrido à sua condição de cor original, o que não foi observado para o nanoparticulado. Além disso, o polimento não retornou a rugosidade de superfície dos compósitos para os valores originais. Os autores concluíram que o polimento da superfície após o clareamento não deve ser a opção de tratamento, uma vez que não foi possível inverter a rugosidade dos compósitos à sua rugosidade original, sugerindo que uma degradação mais extensa e irreversível pode ter ocorrido.

Glutaraldehyde release from heat-polymerized acrylic resins after disinfection and chemical and mechanical polishing

This study evaluated the release of glutaraldehyde from heat-polymerized acrylic resins subjected to disinfection followed by chemical and mechanical polishing. Ninety disc-shaped specimens (15 x 4 mm), 30 per resin (Lucitone 550, QC-20 and Classico), were made and assigned to 2 groups according to the type of polishing. One side of each specimen was not polished and the other was either mechanically (n=45) or chemically (n=45) polished, and immersed in water at 50°C for 1 h to allow the release of intrinsic substances and then kept in distilled water for 7 days. The specimens were disinfected by immersion in 2% glutaraldehyde for 10 min. After this period, 3 specimens from each group were immersed in water for 15, 30, 60, 120 and 240 min. For the 15-, 30-, 60-min immersions, 4 water exchanges were done at the end of period. High performance liquid chromatography (HPLC) was used to detect and quantify the glutaraldehyde released after each period. Data were analyzed statistically by two-way ANOVA and multiple comparisons were done by Tukey’s and Scheffé’s tests (α=0.05). No glutaraldehyde release was observed from the specimens with chemical polishing at any of the immersion periods, while the mechanically polished specimens released glutaraldehyde. In the groups with water exchanges, Lucitone released more disinfectant in the 15-min period (0.040 μg/mL), Classico in the 30-min (0.021 μg/mL) and 60-min (0.018 μg/mL) periods, and QC-20 the same amount (-1.760 μg/mL) in all periods. In the groups without water exchanges, Lucitone released the highest amount of disinfectant (-1.370 μg/mL), differing significantly from QC-20 (0022 g/mL) and Classico (0019 g/mL), which were similar. The findings of this showed that chemically polished specimens from the 3 resin brands did not release glutaraldehyde after different periods of immersion, while glutaraldehyde release was observed from the mechanically polished specimens, especially from those made of Lucitone resin.

Este estudo determinou a liberação de glutaraldeído de resinas acrílicas termopolimerizáveis submetidas a polimento químico e mecânico e desinfetadas. Noventa corpos-de-prova circulares (15 x 4 mm), 30 de cada tipo de resina (Lucitone, QC-20 e Clássico), foram confeccionados e divididos em 2 grupos referentes ao tipo de polimento. Um dos lados de cada corpo-de-prova não foi polido e o outro foi polido mecanicamente (n=45) ou quimicamente (n=45), e imersos em água aquecida a 50°C por 1 h para liberação de substâncias intrínsecas e mantidos em água destilada por 7 dias. A seguir era realizada a desinfecção por imersão em solução de glutaraldeído a 2% por 10 min. Decorrido este período, três corpos-de-prova de cada grupo eram imersos em água por 15, 30, 60, 120 e 240 min. Nos períodos de 15, 30 e 60 min foram realizadas até 4 trocas de água após cada período. As amostras eram analisadas por meio de cromatografia líquida de alta eficiência (HPLC) após cada período. Os dados foram analisados estatisticamente pela Análise de Variância e testes complementares de Tukey e Scheffé (α=0,05). Os corpos-de-prova com polimento químico, de todas as marcas comerciais de resina, não liberaram glutaraldeído em qualquer um dos períodos de imersão em água, enquanto os com polimento mecânico liberaram. Nos grupos com trocas de água, a resina Lucitone liberou maior quantidade de desinfetante nas trocas de 15 min (0,040 μg/mL), a resina Clássico nas de 30 (0,021 μg/mL) e 60 min (0,018 μg/mL) e a QC-20 liberou a mesma quantidade (-1,760 μg/mL), em todos os períodos de imersão em água. Nos grupos sem trocas de água, a resina Lucitone liberou maior quantidade de desinfetante (-1,370 μg/mL), sendo diferente estatisticamente das resinas QC-20 (0,022 μg/mL) e Clássico (0,019 μg/mL), que são similares. Pelos resultados conclui-se que corpos-de-prova polidos quimicamente, das três marcas comerciais de resina, não liberaram glutaraldeído após os diferentes períodos de imersão. Contudo, nos corpos-de-prova polidos mecanicamente houve liberação do desinfetante, com Lucitone liberando maior quantidade em relação às demais resinas estudadas.

Evaluación in vitro de la influencia de sistemas de pulimento intraoral en la rugosidad superficial de una cerámica odontológica después del ajuste / In vitro evaluation of the influence of oral intra polishing systems in the surface roughness of a ceramic dental after adjustment

El objetivo de este estudio fue evaluar tres métodos de pulimento de las superficies de una porcelana con la finalidad de producir superficies con menor rugosidad. Fueron confeccionados 40 especímenes en formato cilindros estandarizados de 5mm de diámetro y 2mm de altura con la porcelana IPS Empress 2. Posteriormente los especímenes fueron divididos en grupos y sus superficies fueron sometidos a técnicas de pulido diferentes. Cada espécimen fue analizado en el rugosímetro, y en cada espécimen se realizó tres mediciones a lo largo de su eje, dando como resultado la rugosidad promedio (Ra). Las medias de Ra fueron sometidas a los tests estadísticos de Anova y Tukey (p? 0,05). El Grupo A (Control - Glaseado) presentó la menor media de Ra (A=0,9190) que los demás grupos (B =2,879; C=2,897; D =3,468). En base a los datos obtenidos por este estudio se puede inferir que los sistemas de pulimento disminuyen la rugosidad superficial provocada por el ajuste oclusal en las cerámicas odontológicas. Entre tanto, esos conjuntos son incapaces de devolver la vitrificación de la superficie

The aim of this study was to evaluate three porcelain polishing systems used to raise smoother surfaces. 40 IPS Empress 2 cilindric specimens with 5mm of diameter and 2mm height. The specimens were divided in groups and polished with different systems. Each specimen has his surface by a perfilometer three times resulting the mean roughness of each specimen (Ra). The Ra mean was submitted to ANOVA and Tukey´s tests (p? 0,05). For the group A (Control - Glaze) was found smaller mean values of Ra (A=0,9190) compared to the other groups (B =2,879; C=2,897; D =3,468). Based on these results we´re able to imply that the used polishing systems reduces the surface roughness caused by occlusal adjustment. However the polishing systems are unable to restore the smoothness provided by the glaze

Effects of different polishing techniques on the surface roughness of dental porcelains

OBJECTIVE: The purpose of this study was to evaluate the effects of different polishing techniques on the surface roughness of dental porcelains. MATERIAL AND METHODS: Fifty-five cylindirical specimens (15x2 mm) were prepared for each feldspathic (Vita VMK 95, Ceramco III) and low-fusing dental porcelain (Matchmaker). Fifty-five specimens of machinable feldspathic porcelain blocks (Vitablocs Mark II), (12x14x18 mm) were cut into 2-mm-thick slices (12x14 mm) with low speed saw. The prepared specimens were divided into 11 groups (n=5) representing different polishing techniques including control ((C) no surface treatment), glaze (G) and other 9 groups that were finished and polished with polishing discs (Sof-Lex) (Sl), two porcelain polishing kits (NTI (Pk), Dialite II (Di)), a diamond polishing paste (Sparkle) (Sp), a zirconium silicate based cleaning and polishing prophy paste (Zircate) (Zr), an aluminum oxide polishing paste (Prisma Gloss) (Pg), and combinations of them. The surface roughness of all groups was measured with a profilometer. The data were analyzed with a 2-way analysis of variance, and the mean values were compared by the Tukey Honestly Significant Difference test (a=0.05). RESULTS: For all porcelain material groups, the lowest Ra values were observed in Group Gl, Group Sl, Group Pk, and Group Di, which were not significantly different from each other (p>0.05).When comparing the 4 different porcelain materials, the machinable feldspathic porcelain block group (Mark II) demonstrated statistically significantly less Ra values than the other porcelain materials tested (p<0.05). No significant difference was observed between the VMK 95 and Ceramco III porcelain groups (p=0.919), also these groups demonstrated the highest Ra values. CONCLUSION: Subjected to surface roughness, the surfaces obtained with polishing and/or cleaning-prophy paste materials used alone were rougher compared to the surfaces finished using Sof-lex, Dialite, ...

Comparison of finishing and polishing systems for residual resin removal after debonding

OBJECTIVE : The aim of this study was to evaluate (1) the effectiveness of one-step polishers on the surface morphology of enamel using scanning electron microscope (SEM) and compare their effects with conventional systems for residual adhesive removal; and (2) the time spent to remove resin remnants. MATERIAL AND METHODS: Metal brackets were bonded to the buccal surface of 80 freshly extracted human premolar teeth and received the same resin-removal methods to evaluate the time spent to remove resin remnants (n=10). The brackets were debonded and residual adhesive was removed using different systems. Fourty-five premolars, including the control group with intact enamel (n=5), were examined by SEM. RESULTS: 30-blade tungsten carbide burs were the least time-consuming procedure. The best system in SEM study was the PoGo micro-polishers followed by Super-Snap Rainbow system. CONCLUSIONS: The effect of polishing systems on residual resin removal was dependent on the characteristics of the instruments in each system.

Tensile bond strength of composite luting cements to metal alloys after various surface treatments.

Aims: To evaluate the effects of two different surface treatments and bonding agents on tensile bond strength between a Co-Cr and a Ni-Cr cast alloy and two resin-luting cements. Materials and Methods: Two hundred and forty alloy samples were cast and subjected to surface treatments such as sandblasting, chemical etching, and sandblasting plus chemical etching. Panavia F and CandB cement were used as cementing mediums. The etching qualities were examined by a stereooptic microscope. Failure surfaces were examined throughout scanning electron microscopy. The data were evaluated using statistical methods, namely analysis of variance and multiple comparison test (Tukey HSD). Results: Significant differences were found in the bonding provided by the various cements (P < 0.001) and also type of surface treatments (P < 0.001). For all groups, sandblasted surfaces showed the highest bond strength values. There was no significant difference between the Cr-Co and the Cr-Ni alloys (P > 0.05). Conclusions: Panavia F showed higher tensile strength and the sandblasted samples possessed higher tensile strength.

Surface roughness of a dental ceramic after polishing with different vehicles and diamond pastes

During fabrication of bonded ceramic restorations, cervical adaptation, occlusal adjustment and final finishing/polishing are procedures to be performed at the dental office after adhesive cementation. Final adjustments may result in loss of ceramic glaze, which requires new polishing of the ceramic surface, with special attention for selection of adequate materials and instruments. The purpose of this study was to evaluate the efficiency of different vehicles associated with diamond pastes indicated for dental ceramic polishing. Two polishing pastes (Crystar Paste and Diamond Excell) associated with four vehicles (rubber cup, Robinson bristle brush, felt wheel and buff disc) were evaluated. Disc-shaped specimens were fabricated from Ceramco II dental ceramic. Surface roughness means (Ra) of the ceramic specimens were determined with a rugosimeter. Data were analyzed statistically by two-way ANOVA and Tukey's test at 5 percent significance level. There was no statistically significant difference (p>0.01) between the polishing pastes. However, there were statistically significant differences (p<0.01) among the tested vehicles. Vehicle-paste interaction showed statistically significant difference (p<0.05) as well. It may be concluded that: 1) Robinson bristle brush, felt wheel and buff disc were efficient vehicles to be used in association with a diamond polishing paste; 2) The use of rubber cup as a vehicle showed poor efficiency for mechanical polishing of the ceramic surfaces; 3) Both pastes provided similar and efficient polishing and may be recommended for use with an appropriated vehicle.

Durante a confecção de restaurações de cerâmica aderidas, a adaptação cervical, o ajuste oclusal e o polimento/acabamento final são procedimentos a serem executados no consultório odontológico após a cimentação adesiva. Os ajustes finais podem resultar na perda do "glaze" da cerâmica, o que requer novo polimento da superfície da restauração, necessitando de atenção especial em relação aos materiais e instrumentos adequados. O objetivo deste estudo foi avaliar a eficiência de diferentes veículos associados a pastas diamantadas indicadas para polimento de cerâmicas odontológicas. Duas pastas de polimento diamantadas (Crystar Paste and Diamond Excell) associadas a quatro veículos (taça de borracha, escova de Robinson, roda de feltro e disco de feltro) foram avaliadas. A cerâmica Ceramco II foi selecionada para a confecção dos espécimes. A rugosidade superficial (Ra) dos espécimes de cerâmica foi determinada por um rugosímetro. Os dados foram submetidos a análise de variância a dois critérios e ao teste de Tukey com nível de significância de 5 por cento. Não houve diferença estatisticamente significante (p>0,01) entre as pastas de polimento avaliadas. Contudo, houve diferença significante (p<0,01) entre os veículos. A interação veículo-pasta revelou diferença significante (p<0,05). Conlcuir que: 1) A escova de Robinson, a roda de feltro e o disco de feltro foram veículos efetivos para serem usados em associação com as pastas de diamante; 2) O uso da taça de borracha como veículo foi menos eficiente para o polimento mecânico das superfícies cerâmicas; 3) Ambas as pastas de polimento apresentaram comportamento similar e eficiente e podem ser indicadas para o polimento final de restaurações cerâmicas com um veículo apropriado.

Polishing methods of an alumina-reinforced feldspar ceramic

The purpose of this study was to test the hypothesis that mechanical polishing methods of ceramic surfaces allow similar superficial roughness to that of glazed surfaces. Twenty-five Vitadur Alpha ceramic discs (5 mm x 2 mm) were prepared according to the manufacturer's specifications. All specimens were glazed and randomly assigned to 5 groups (n=5), according to finishing and polishing protocols: G1: glazed (control); G2: diamond bur finishing; G3: G2 + silicon rubber tip polishing; G4: G3 + felt disc/diamond polishing paste; G5: G3 + felt disc impregnated with fine-particle diamond paste. Next, surface roughness means (Ra - æm) were calculated. Qualitative analysis was made by scanning electron microscopy. Surface roughness data were submitted to ANOVA and Tukey's test at 5 percent significance level. G1 and G4 were statistically similar (p>0.05). G2 presented the highest roughness means (p<0.05) followed by groups G3, G5, G4 and G1 in a decreasing order. The hypothesis was partially confirmed as only the mechanical polishing (G4) produced similar superficial roughness to that of surface glazing, although finishing and polishing are technically critical procedures.

O objetivo deste estudo foi testar a hipótese de que o acabamento e o polimento da superfície cerâmica produzem rugosidade superficial semelhante à superfície cerâmica vitrificada. Vinte e cinco corpos-de-prova (5 mm x 2 mm) da cerâmica Vitadur Alpha foram obtidos de acordo com as recomendações do fabricante. Todas os corpos-de-prova foram vitrificados e aleatoriamente divididos em 5 grupos (n=5), de acordo com os seguintes protocolos de acabamento e polimento: G1: vitrificação (controle); G2: abrasão com ponta diamantada; G3: G2 + acabamento com borrachas abrasivas; G4: G3 + polimento com pasta diamantada/disco de feltro; G5: G3 + disco de feltro impregnado com pasta diamantada. Após 6 análises individuais foi obtida 1 média por corpo-de-prova da rugosidade (Ra). A análise qualitativa foi realizada por microscopia eletrônica de varredura. Os valores médios de rugosidade foram submetidos à ANOVA e ao teste de Tukey com nível de significância de 5 por cento. G1 e G4 foram estatisticamente semelhantes (p>0.05). O grupo G2 apresentou o maior valor médio de rugosidade (p<0.05) seguido por G3, G5, G4 e G1 em ordem decrescente. A hipótese foi parcialmente confirmada, pois somente o polimento mecânico do grupo G4 produziu rugosidade superficial semelhante à da superfície vitrificada, embora o acabamento e o polimento sejam procedimentos críticos tecnicamente.

Effect of different finishing and polishing techniques on the surface roughness of microfilled, hybrid and packable composite resins

Este estudo avaliou a rugosidade superficial (Ra, µm) de 2 resinas compostas microparticuladas (Durafill; Perfection), 1 híbrida (Filtek Z250) e 2 compactáveis (Surefil; Fill Magic), antes (baseline) e após a realização de 8 técnicas de acabamento e polimento. A rugosidade foi avaliada com rugosímetro. Dez espécimes de cada resina foram submetidos aos seguintes procedimentos: A - brocas cabide; B - pontas diamantadas fina/extrafina; C - sistema Sof-Lex; D - sistema Super-Snap; E - pontas de borracha + pastas de polimento; F - pontas diamantadas + pontas de borracha + pastas de polimento; G - pontas diamantadas + Sof-Lex; H - pontas diamantadas + Super-Snap. Os dados foram submetidos à análise de variância a dois critérios e teste de Tukey. Foi observada diferença estatisticamente significante (p<0.05) tanto entre as resinas compostas quanto entre as técnicas de acabamento/polimento. Para todas as resinas, a maior rugosidade foi produzida com o emprego das pontas diamantadas (Ra: 0.69-1.44 µm). O menor valor de rugosidade foi obtido com o sistema Sof-Lex (Ra: 0.11- 0.25 µm). A Durafill apresentou melhor lisura que a Perfection e a Z250, que apresentaram melhor lisura que as resinas compactáveis. A seqüência completa de discos Sof-Lex produziu a melhor lisura para todas as resinas. Em áreas sem acesso aos discos, as pontas de borracha e pastas de polimento produziram lisura de superfície satisfatória para as resinas híbridas enquanto as brocas carbide produziram polimento adequado para as resinas compactáveis.

Surface roughness of composite resins after finishing and polishing

This study evaluated the effect of surface finishing methods on the average surface roughness of resin composites. Seven composites and two polishing systems were used. One hundred and twenty-six conical specimens of each material were prepared in stainless steel molds against a polyester strip. Forty-two of them remained intact and were used as controls. Each half of the remaining samples was polished with either diamond burs or diamond burs + aluminum oxide discs. The results showed no statistical difference in average surface roughness (Ra, µm) between the polyester strip and aluminum oxide discs (p>0.05). However, finishing with diamond burs showed a statistically higher average roughness for all composites (p<0.05). Statistical differences were detected among materials (p<0.05) in the use of diamond burs

Textura superficial e manchamento de alguns materiais restauradores estéticos. Efeito do acabamento / Suface texture and staining of some aesthetic dental materials. Effect of the finishing process

A pesquisa avaliou alguns materiais estéticos quanto à textura de superfície, antes e após diferentes técnicas de acabamento, bem como o manchamento dos materiais por corante alimentar. Foram estudados três compômeros, um ionômero de vidro e duas resinas compostas. Após a análise em MEV, os materiais estudados se apresentavam com porosidades e asperezas. Os discos SofLex e as brocas multilaminadas ofereceram melhor acabamento de superfície. Todos os materiais estudados tiveram manchamento considerável com corante alimentar, após 72 horas de imersäo

Superfície radicular - instrumentaçäo manual, aplicaçäo do jato de bicarbonato de sódio e polimento. Análise em microscopia eletrônica de varredura / Root surface - manual instrumentation, use of air powder abrasive system and polishing. A scanning ellectron microscopy study

Este estudo teve como objetivo avaliar através da microscopia eletrônica de varredura o efeito do polimento com pastas de diferentes abrasividades, sobre superfície radiculares após instrumentaçäo manual associada a aplicaçäo do jato de bicarbonato de sódio. Utilizou-se 39 superfícies radiculares que foram divididas em 5 grupos: I controle (somente raspagem), II raspagem e aplicaçäo de jato de bicarbonato de sódio, III raspagem, aplicaçäo de jato de bicarbonato de sódio e polimento compasta de granulaçäo fina, IV raspagem, aplicaçäo de jato de bicarbonato de sódio e polimento com pasta de granulaçäo grossa e V raspagem, aplicaçäo de jato de bicarbonato de sódio e polimento com pasta de granulaçäo grossa seguida com pasta de granulaçäo fina. A raspagem foi realizada com curetas de Gracey n§ 5-6, com 40 movimentos de traçäo no sentido ápico-cervical e tanto o jato de bicarbonato de sódio como as pastas foram aplicadas por 10 segundos. Os grupos I, IV e V apresentaram graus intermediários de irregularidade de superfície, enquanto que o grupo II - maiores graus e o grupo III - menores graus...

Cambios histológicos en la pulpa dental, ocasionados por preparaciones protésicas empleando abrasivos de diamante vs carburo / Histological changes in dental pulp produced by dental preparation for prosthesis application, in comparison between reaming by diamond or carbide tips

Este estudio se realizó en 30 dientes, todos terceros molares superiores, los cuales se prepararon con el método para aplicación de prótesis, para investigar daño pulpar. La pulpa como es sabido es un órgano sensible a cualquier agente externo; el tallado dental puede en alguna forma lesionar estructuras dentales (dentina, pulpa). Se determinaron los cambios ocurridos en la pulpa dental provocados por un desgaste protésico. El grupo se subdividió en 3 de 10 cada uno; en el primero se hizo extracción sin desgaste, en el segundo desgaste con diamante y extracción. La preparación de los órganos dentarios fue con irrigación constante; al término de la misma, se colocó una prótesis provisional de acrílico con matriz de acetato al vacío y cementado con óxido de zinc y eugenol. Por medio del microscopio de luz a las 24 horas post-tallado se pusieron en evidencia cambios histológicos que consistieron en congestión vascular, incremento de fibroblastos, fibras colágenas y datos inflamatorios sólo en uno de los grupos investigados que fue el rimado con carburo